Silver-plated polyamide fabrics with high electromagnetic shielding effectiveness performance prepared by in situ reduction of polydopamine and chemical silvering

In this article, the silver-plated polyamide fabrics (SPPAFs) with high electroconductibility and shielding effectiveness were fabricated by using in situ reduction of polydopamine and chemical silvering. The effects of SPPAFs dopamine (C₈H₁₁O₂N) and silver nitrate (AgNO₃) concentration on surface resistivity and electromagnetic interference shielding effectiveness were studied. The results showed that the surface resistivity of SPPAFs can reach a minimum value of 0.06 ± 0.014 Ω cm⁻¹, when C₈H₁₁O₂N concentration is 4 g L⁻¹ and the AgNO₃ concentration is 120 g L⁻¹. The shielding effectiveness of SPPAFs in the wide frequency range of 10–3000 MHz increases with the increase in the concentration of AgNO₃, and increases first and stabilizes afterward with increasing C₈H₁₁O₂N concentration. When the concentration of C₈H₁₁O₂N and AgNO₃ is 3 and 120 g L⁻¹, respectively, mean shielding effectiveness values in the low-, medium-, and high-frequency bands are 71.3, 73.8, and 76.1 dB, respectively. Moreover, the mean shielding effectiveness values is 83.79 dB in the frequency range of 1.2–2.3 GHz. The dominant shielding mechanism of SPPAFs is the reflected electromagnetic waves and the absorption shielding effectiveness is less than 2 dB. The average electromagnetic shielding values of SPPAFs are above 67 dB after 16 weeks of storage, when C₈H₁₁O₂N concentration is 4 g L⁻¹ and the AgNO₃ concentration is 80 and 100 g L⁻¹. The prepared SPPAFs show promising applications in military textiles and smart wearable clothing. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 48227.     

A new perspective of co-doping and Nd segregation effect on proton stability and transportation in Y and Nd co-doped BaCeO3

Bulk and surface properties of proton stability and transportation in Y and Nd co-doped BaCeO₃ (BCYN), especially the effect of Nd segregation, were investigated by first-principles calculations. Since the structure of doped BaCeO₃ at the operating temperature of proton-conducting has been unclear for a long time, we have summarized the latest experimental results and calculated the structure of the asymmetric BCYN for the first time. The results show that compared with Y, Nd doping promotes oxygen vacancy formation, however reduces proton stability. Our calculation can also provide a possible explanation for the formation of space charge layer at the grain boundary of doped BaCeO₃ in experiment. Unlike the stable Y in BCYN, Nd is calculated to be easily segregated, which can facilitate both proton hydration and proton transportation near the surface. Moreover, Nd segregation at the grain boundary is predicted to be beneficial for proton transportation between grains.     

Rapid screening of DON contamination in whole wheat meals by Vis/NIR spectroscopy and computer vision coupling technology

This work intends to develop an online experimental system for screening of deoxynivalenol (DON) contamination in whole wheat meals by visible/near-infrared (Vis/NIR) spectroscopy and computer vision coupling technology. Spectral and image information of samples with various DON levels was collected at speed of 0.15 m s⁻¹ on a conveyor belt. The two-type data were then integrated and subjected to chemometric analysis. Discriminant analysis showed that samples could be classified by setting 1000 μg kg⁻¹ as the cut-off value. The best correct classified rate obtained in prediction was 93.55% based on fusion of spectral and image features, with reduced prediction uncertainty as compared to single feature. However, quantification of DON by quantitative analysis was not successful due to poor model performance. These results indicate that, although not accurate enough to provide conclusive result, this coupling technology could be adopted for rapid screening of DON contamination in cereals and feeds during processing.     

Ni-Foam Structured Ni-Phyllosilicate Ensemble as an Efficient Monolithic Catalyst for CO2 Methanation

This work proposed a new path to synthesize Ni-phyllosilicate through the reaction of nickel hydroxide and silica sol on the surface of Ni-foam to form the monolithic Ni-phyllosilicate/Ni-foam catalyst. Ni-phyllosilicate could reprint the morphology of nickel hydroxid and firmly anchor on the framework of Ni-foam, which obtained fine Ni particles of 2.8 nm after reduction in H₂ at 650 °C, resulting in high catalytic activity for CO₂ methanation. In addition, the Ni-phyllosilicate/Ni-foam catalyst showed high long-term stability in a 100 h-lifetime test owing to the combined effects of surface confinement of Ni-phyllosilicate, firm anchoring between Ni-phyllosilicate and Ni-foam, as well as the high heat transfer property of Ni-foam.

Graphical Abstract

     

A highly active composite electrocatalyst Ni–Fe–P–Nb2O5/NF for overall water splitting

This work demonstrates a facile Nb₂O₅-decorated electrocatalyst to prepare cost-effective Ni–Fe–P–Nb₂O₅/NF and compared HER & OER performance in alkaline media. The prepared electrocatalyst presented an outstanding electrocatalytic performance towards hydrogen evolution reaction, which required a quite low overpotential of 39.05 mV at the current density of ?10 mA cm^?2 in 1 M KOH electrolyte. Moreover, the Ni–Fe–P–Nb₂O₅/NF catalyst also has excellent oxygen evolution efficiency, which needs only 322 mV to reach the current density of 50 mA cm^?2. Furthermore, its electrocatalytic performance towards overall water splitting worked as both cathode and anode achieved a quite low potential of 1.56 V (10 mA cm^?2).     

Design and synthesis of side-chain optimized poly(2,6-dimethyl-1,4-phenylene oxide)-g-poly(styrene sulfonic acid) as proton exchange membrane for fuel cell applications: Balancing the water-resistance and the sulfonation degree

Side-chain optimized poly (2,6-dimethyl-1,4-phenylene oxide)-g-poly (styrene sulfonic acid) (PPO-g-PSSA) is designed with balanced water-resistance and sulfonation degree. The PPO-g-PSSA is synthesized by controlled atom-transfer radical polymerization (ATRP) from brominated poly (2,6-dimethyl-1,4-phenylene oxide) (PPO-xBr) and ethyl styrene-4-sulfonate and followed by hydrolysis. A series of PPO-g-PSSA are prepared possessing different bromination degree (x) of PPO-xBr and polymerization degree (m) of the side-chains and the water-resistances of the fabricated membranes are investigated. The results show that a PPO-g-PSSA at relatively low x (x < 0.2) and high m (m > 4) exhibits good balance between the water-resistance and the sulfonation degree. Namely, it displays suitable proton conductivity with compromised water-resistance. Moreover, a maximum ion exchange capacity (IEC) of 3.24 mmol g^?1 is reached without the sacrifice of water-resistance. In addition, PPO-g-0.08PSSA-13 and PPO-g-0.14PSSA-4 are chosen characterized by thermogravimetric analysis, proton conductivities and mechanical properties. At 90% RH, the optimized PPO-g-0.08PPSA-13 possesses a proton conductivity of 37.9 mS cm^?1 at 40 °C and 45.5 mS cm^?1 at 95 °C, respectively.     

Cyclic thermal shock resistance of h-BN composite ceramics with La2O3–Al2O3–SiO2 addition

The effects of La₂O₃–Al₂O₃–SiO₂ addition on the thermal conductivity, coefficient of thermal expansion (CTE), Young's modulus and cyclic thermal shock resistance of hot-pressed h-BN composite ceramics were investigated. The samples were heated to 1000 °C and then quenched to room temperature with 1–50 cycles, and the residual flexural strength was used to evaluate cyclic thermal shock resistance. h-BN composite ceramics containing 10 vol% La₂O₃–Al₂O₃ and 20 vol% SiO₂ addition exhibited the highest flexural strength, thermal conductivity and relatively low CTE, which were beneficial to the excellent thermal shock resistance. In addition, the viscous amorphous phase of ternary La₂O₃–Al₂O₃–SiO₂ system could accommodate and relax thermal stress contributing to the high thermal shock resistance. Therefore, the residual flexural strength still maintained the value of 234.3 MPa (86.9% of initial strength) after 50 cycles of thermal shock.     

Mesoporous Co–Mn Spinel Oxides as Efficient Catalysts for Low Temperature Propane Oxidation

Catalysis Letters - A series of mesoporous cobalt–manganese catalysts were successfully synthesized by sol–gel method as efficient catalysts for the propane oxidation. A significant...     

Data sharing mechanism of various mineral resources based on blockchain

Basins with various mineral resources coexisting and enriching often occupy an important strategic position. The exploration of various mineral resources is repetitive at present due to unshared data and imperfect management mechanism. This situation greatly increases the cost of energy exploitation in the country. Traditional data-sharing mode has several disadvantages, such as high cost, difficulty in confirming the right of data, and lack of incentive mechanism, which make achieving real data sharing difficult. In this paper, we propose a data-sharing mechanism based on blockchain and provide implementation suggestions and technical key points. Compared with traditional data-sharing methods, the proposed data-sharing mechanism can realize data sharing, ensure data quality, and protect intellectual property. Moreover, key points in the construction are stated in the case study section to verify the feasibility of the data-sharing system based on blockchain proposed in this paper.